Long term exposure type was improved the defect, the degradation of corrosion, and the improved version shows excellent heat and corrosion resistance even if heat is charged after the long term outdoor exposure at room temperature.

Characteristics

  • Feasible to use at the object temperature from 100 - 600℃.(Silicoue resin type)
  • Excellent corrosion resistance at RT before bake.
  • One-component type and excellent workability by brush , roller & spray.

Application

Applicable to the plant and exporting equipment which needs long term after coating before plant operation.

Package

15㎏, 4㎏ (Designated thinner : 16L, 4L)

Product Line up
Product name
(Heat-resistant temp)		 Color DFT Dilution ratio
(wt%)		 Std usage
(/㎡)		 Coating interval (20℃)
㎛/time Brush
Roller		 Spray Brush
Roller		 Spray Minimum Maximum
SL-100
(max100℃)
SL-200
(max200℃)
SL-300
(max300℃)		 Primer Gray
Red rust		 20㎛ 5 - 10 5 - 20 0.15㎏ 0.20㎏ min
4Hours		 max
30days
Top coat Silver 10㎛ 0 - 3 0 - 3 0.11㎏ 0.16㎏ ↑ ↑
Special color 20㎛ 5 - 10 5 - 20 0.15㎏ 0.20㎏ ↑ ↑
SL-400
(max400℃)
SL-600
(max600℃)		 Primer Gray
Red rust		 20㎛ 5 - 10 5 - 20 0.15㎏ 0.20㎏ min
4Hours		 max
30days
Top coat Silver 10㎛ 0 - 3 0 - 3 0.11㎏ 0.16㎏ ↑ ↑
Special color 20㎛ 5 - 10 5 - 20 0.15㎏ 0.20㎏ ↑ ↑
  • Apply SL thinner for dilution.
  • DFT (Dry Film Thickness) : Minimum film thickness to secure property.
  • Above products are made to order.
  • Basically these products are applied for outer only hence it may not be feasible to maintain enough property if applied for inner.
Basic coating specification (example of specification from 100 - 300℃)
Process Applicable Paint Coating time Coating method Std thickness (Silver/Special color)
Substrate treatment ISO std : Sa min2.5 Blast shot (If impossible, apply ISO std : St min3.0)
1st U/C HEATOP SL-300 Primer Gray 1 time Brush / Roller or Spray 20㎛
2nd U/C HEATOP SL-300 Primer Gray 1 time Brush / Roller or Spray 20㎛
1st T/C HEATOP SL-300 Top coat (Silver/Special color) 1 time Brush / Roller or Spray (10/20㎛)
2nd T/C HEATOP SL-300 Top coat (Silver/Special color) 1 time Brush / Roller or Spray (10/20㎛)
Basic coating specification (example of specification from 400 - 600℃)
Process Applicable Paint Coating time Coating method Std thickness (Silver/Special color)
Substrate treatment ISO std : Sa min2.5 Blast shot
1st U/C HEATOP SL-600 Primer Gray 1 time Brush / Roller or Spray 20㎛
2nd U/C HEATOP SL-600 Primer Gray 1 time Brush / Roller or Spray 20㎛
1st T/C HEATOP SL-600 Top coat (Silver/Special color) 1 time Brush / Roller or Spray (10/20㎛)
2nd T/C HEATOP SL-600 Top coat (Silver/Special color) 1 time Brush / Roller or Spray (10/20㎛)
Caution on the application of Long term exposure type
  1. Substrate surface treatment : Remove oil from substrate surface by thinner then implement blast shot, ISO Sa 2.5 min.
    In case that blast shot is not feasible, apply sanding machine and remove foreign matters such as black scale, old paint film, and rust then implement surface treatment better than ISO St.3.0 .
    After treatment of substrate, remove dirts by air blow then implement undercoat application.
    For 400℃ and 600℃ type, implement a blast shot better than ISO Sa 2.5 .
  2. Refrain from applying at below 5℃ or humidity higher than 85%.
  3. SZ-1200 is applied by airless spray after blast shot. (Better than ISO Sa 2.5)
  4. In case that Spray interval is out of specification, too long, apply sanding to obtain rough surface then implement application.
  5. Paint usage is fluctuated by shape of coating object, surface condition, and coating condition.
  6. When can is opened, confirm the condition of settling in the bottom then agitate well to be homogenious.
  7. Store in a dangerous goods warehouse with tightly sealed at good ventilation and prohibition of flame.