«Heat-resistant paint applied during heating»
This product is applied while object is being heated.
Since heat is being generated, this product is applied over poorly treated object.
Hence main application of this product is temporary repair and there is a problem on long term durability.
Also there is a limit for applicable temperature.
Application
Temporary repair while plant equipment is being heated.
Package
15㎏, 4㎏ (Designated thinner : 16L, 4L)
| Heat-resistant temp | Product name | Color | DFT | Dilution ratio (wt%) |
Std usage (/㎡) |
Coating interval (20℃) |
|||
|---|---|---|---|---|---|---|---|---|---|
| ㎛ /time | Brush Roller |
Spray | Brush Roller |
Spray | Min | Max | |||
| Max 200℃ |
Z-150 primer | Gray | - | 5 - 20 | 5 - 20 | Paint usage depends on temparature at spray. Guideline is for primer 0.25-0.30㎏ and for top coat Silver 0.17-0.22㎏. |
- | max 1day |
|
| Z-150 Top coat | Silver | - | 5 - 15 | 5 - 15 | - | max 1day |
|||
| Max 600℃ |
Z-250 primer | Gray | - | 5 - 20 | 5 - 20 | - | max 1day |
||
| Z-250 Top coat | Silver | - | 5 - 15 | 5 - 15 | - | max 1day |
|||
- Apply Z-thinner for dilution.
- DFT (Dry Film Thickness) : Minimum film thickness to secure property.
- Above products are made to order.
- (Note) Coating feasible temperature is 120℃ for Z-150 and 200℃ for Z-250.
- Basically these products are applied for outer only hence it may not be feasible to maintain enough property if applied for inner.
«Rapid heating type»
When high temperature is charged on wet film, remained solvent in wet film will evaporate and bubble is generated in wet film.
In case bubble is generated, degradation of film is accelarated and as a result, corrosion resistance is degraded.
Rapid heating type can prevent bubble generation and durability of film is maintained same level as Standard type.
Application
Rapid heating equipment, maffler of automobile, and exhaust of generator.
Package
15㎏, 4㎏ (Designated thinner : 16L, 4L)
| Heat- resistant temp |
Product name | Color | DFT | Dilution ratio (wt%) |
Std usage (/㎡) |
Coating interval (20℃) |
|||
|---|---|---|---|---|---|---|---|---|---|
| ㎛ /time | Brush Roller |
Spray | Brush Roller |
Spray | Min | Max | |||
| Max 600℃ |
HN-600 Primer | Gray | 20㎛ | 0 - 10 | 5 - 25 | 0.15㎏ | 0.20㎏ | min 4Hours |
max 7days |
| HN-600 Top coat | Silver | 10㎛ | 0 - 10 | 5 - 25 | 0.11㎏ | 0.16㎏ | ↑ | ↑ | |
| Black | 20㎛ | 5 - 10 | 5 - 20 | 0.15㎏ | 0.20㎏ | ↑ | ↑ | ||
- Apply HN thinner for dilution.
- DFT (Dry Film Thickness) : Minimum film thickness to secure property.
- Above products are made to order.
- Basically these products are applied for outer only hence it may not be feasible to maintain enough property if applied for inner.